Diamond-Like Coatings for Friction Units of Space Applications

When developing materials for moving joints and friction units operating in outer space, the wear resistance of friction pairs with friction coefficients from 0.05 to 0.1 is of particular importance. The values of the friction coefficients determine the heating of the interfaces and the power of the drives. Wear resistance regulates the service life of friction units. The choice of diamond-like coatings as one of the elements of the friction pair determines the high wear resistance of the interface when working with solid lubricant coatings due to their high chemical inertness and the absence of substance transfer from the solid lubricating coating to the diamond-like coating. This paper presents the results of testing diamond-like coatings during friction on the solid lubricant coating EONIT-3 and tests in air and vacuum up to 10^–6 mm Hg. according to the shaftbushing scheme in the temperature range from –50 ℃ to +50 ℃. A diamond-like single-crystalline coating 20 microns thick was applied to a shaft made of hardened steel ShKh-15; EONIT-3 coating with a thickness of 15 microns is applied to a steel bushing. Tests were carried out under a normal load of 100 N; shaft rotation speed — 200 rpm; sliding speed — 0.12 m/s; test duration 1 hour. The friction coefficients and wear of the solid lubricant coating were measured. No wear of the diamond-like coatings was detected. The wear of the solid lubricant coating ranged from 1.065×10^–8 mm³/m to 3.195×10^–8 mm³/m at temperatures from –50 ℃ to +50 ℃ in air and in a vacuum of 10^–6 mm Hg.

1. Bronovets М.А. Tribologicheskie pokrytiya dlya otkrytogo kosmosa // Friction and Wear. — 2023 (44), no. 6, 544—550 (in Russian)

2. Bronovets М.А. Tribotechnicheskie characteristiki tverdych smasochnych pokrytii // Friction and Wear. — 2023 (44), no. 4, 335—341 (in Russian)

3. Deryaguin B.V. Spitsyn B.V. Khimicheskaya kristallizaziya Almaza // Rost kristallov. Erevan: Erevansky gosuniversitet. — 1977 (12), 28—32 (in Russian)

4. Spitsyn B.V., Bouilov L.L., and Deryaguin B.V. Vapor Growth of Diamond on Diamond and Other Surfaces // Crystal Growth. — 1981 (52), 219—221

5. Donnet C. and Erdemir A. Diamond-Like Carbon Films: A Historical Overview // Tribology of Diamond Like Carbon Films. Fundamentals and Applications / ed. by С. Donnet and A. Erdemir. — NY: Springer. — 2008, 1—13

6. Bewilogua K. and Hofmann D. History of Diamond-Like Carbon Films – from First Experiments to Worldwide Applications // Surface and Coatings Technology. — 2014 (242), 214—225

7. Tyagi Ankit, Walia R.S., Murtaza Qasim, et al. A Critical Review of Diamond Like Carbon Coating for Wear Resistance Applications // International Journal of Refractory Metals&Hard Materials. — 2019 (78), 107—122

8. Georgakilas V., Perman J.A., Tucek J., and Zboril R. Broad Family of Carbon Nanoallotropes: Classification, Chemistry and Applications of Fullereness, Carbon Dots, Nanotubes, Graphene, Nanodiamonds and Combined Superstructures // Chemical Reviews. — 2015 (115), no. 11, 4744—4822

9. Vetter J. 60 Years of DLC Coatings: Historical Highlights and Technical Review of Cathodic Arc Processes to Synthesize Various DLC Types, and Their Evolution for Industrial Applications // Surface and Coatings Technology. — 2014 (257), 213—240

10. Gayathri S., Kumar N., Krishnan R., Ravindran T.R, Amirthapandian S., Dash S., Tyagi A.K., and Sridharan M. Influence of Transition Metal Doping on the Tribological Properties of Pulsed Laser Deposited DLC Films // Ceramics In-ternational. — 2015 (41), no. 1, Part B, 1797—1805

11. Erdemir A. and Fryilmaz O. On the Intrinsic and Extrinsic Hydrogen Lubrication Mechanism of Various Carbon Films: An Imaging TOF-SIMS Study // World Tribology Congress 2009. Kyoto, Japan, September 6-11. — 2009, 431, K-223

12. Levchenko V.A., Buyanovskii I.A., Samysenko V.D. Issledovanie almasopodobnogo monokristallicheskogo uglerodnogo pokrytiya dlya tribologicheskogo primeneniya // Friction and Wear. — 2021 (42), no. 6, 670—680 (in Russian)

13. Shkalei I.V., Muravyeva T.I., Mezrin A.M. Svyaz’ morfologii I chimicheskogo sostava poverkhnosty legirovannych almasopodobnych pokrytii s koefficientom treniya // Friction and Wear. — 2021 (42), no. 6, 670—680