Features of Deterioration of the Contact Surface of C235 Steel and Its Wear in Dry Sliding Against Steel under Alternating Current

Dry sliding of model samples of C235 steel against 45 steel under alternating current with a density of up to 120 A/cm2 using the pin-on-ring configuration was investigated. The possibilities of increasing wear resistance by changing one of the geometric parameters (height) of the sample (pin) were studied and the temperature of the sample holder at different points was investigated. It was shown that this temperature can exceed 150 ℃ in the sample mounting zone. The increase in the temperature of the sample holder and the wear intensity were nonlinear in accordance with a curve close to an exponential function with increasing current density. Sliding at a current density higher than 100 A/cm2 occurred under conditions of catastrophic wear. Formation of a transfer layer with a thickness of about 20 μm was observed on the contact surface of the samples. Using X-ray phase analysis, it was found that the transfer layer contains more than 70 % FeO. The analysis of wear surfaces allowed to reveal the mechanism of contact layers deterioration, which was presented as the division of the nominal contact area into two sectors. The boundary between the sectors was quite clear and perpendicular to the sliding direction. The sector directed towards the oncoming contact surface of the counterbody had traces of adhesion, plowing, etc., which usually appear during sliding without current. The other sector had signs of deformation similar to the deformation of a viscous liquid. Traces of adhesion were not observed here. The friction coefficient decreased with increasing current density and did not change its behavior upon transition to the catastrophic wear mode. The presented regularities were observed at a qualitative level regardless of the height of the samples. Only the heating temperatures of the sample holder differed quantitatively. The results of the work will be useful in creating a real friction unit operating in sliding current collection with a high current density.

1. Kragelsky I.V., Dobychin M.N., and Kombalov V.S. Friction and Wear Calculation Methods. — New York: Pergamon Press. — 1982

2. Bowden F.P. and Tabor D. Friction: An Introduction to Tribology. — Anchor, New York: Anchor Press. — 1973

3. Sosnovskiy L.A. Tribo-Fatigue: Wear-Fatigue Damage and Its Prediction. — Verlag, Berlin, Heidelberg: Springer. — 2005

4. Wang X., Song K., Duan J., Feng Ji., Huang T., and Xing Ji. Current-Carrying Tribological Behavior and Wear Mechanism of CuW Composites with Different W Content // Tribol. Int. — 2024 (200), 110125. https://doi.org/10.1016/j.triboint.2024.110125

5. Aleutdinova M.I. and Fadin V.V. Influence of the FeO Presence in the Contact Space on the Character of Dry Sliding of Metals under Electric Current // AIP Conf. Proc. — 2023 (2899), 020006. https://doi.org/10.1063/5.0162747

6. Wang S.Q., Wei M.X., and Zhao Y.T. Effects of the Tribo-Oxide and Matrix on Dry Sliding Wear Characteristics and Mechanisms of a Cast Steel // Wear. — 2010 (269), 424. http://dx.doi.org/10.1016/j.wear. 2010.04.028

7. Aleutdinova M.I. and Fadin V.V. Variations in the Contact Layer Structure of Low-Carbon Steel in Sliding Against a Steel Counterbody with Different Nominal Contact Areas under a High-Density Electric Current // Russ. Phys. J. — 2023 (66), no. 6, 605—611. DOI 10.1007/s11182-023-02982-53

8. Waseda Y., Matsubara E., and Shinoda K. X-Ray Diffraction Crystallography. Introduction, Examples and Solved Problems. — London, New York: Springer Heidelberg Dordrecht, Springer-Verlag Berlin Heidelberg. — 2011. DOI 10.1007/978-3-642-16635-8

9. Wang S.Q., Wang L., Zhao Y.T., Sun Y., and Yang Z.R. Mild-to-Severe Wear Transition and Transition Region of Oxidative Wear in Steels // Wear. — 2013 (306), 311—320. http://dx.doi.org/10.1016/j.wear.2012.08.017

10. Cao L., Hou C., Tang F., Liang S., Luan J.,Jiao Z. et al. Thermal Stability and High-Temperature Mechanical Performance of Nanostructured W-Cu-Cr-ZrC Composite // Compos. B. — 2021 (208), 108600. https://doi.org/10.1016/j.compositesb.2020.108600

11. Fadin V.V., Aleutdinova M.I., and Kolubaev A.V. Effect of High-Density Electric Current on Wear and Average Temperature of Steel/Steel Triboelectric Contact // J. Friction and Wear. — 2018 (39), no. 4, 294— 298. http://dx.doi.org/10.3103/S1068366618040050 12. Gao G.Q., Wu G.N., and Zhang W.H. Experimental Research on the Friction and Wear Properties of a Contact Strip of a Pantograph–Catenary System at the Sliding Speed of 350 km/h with Electric Current // Wear. — 2015 (332-333), 949—955. http://dx.doi.org/10.1016/j.wear.2014.11.004

12. Madah F., Dehghanian Ch., and Amadeh Ah.Ali. Investigations on the Wear Mechanisms of Electroless Ni–B Coating During Dry Sliding and Endurance Life of the Worn Surfaces // Surface & Coatings Technology. — 2015 (282), 6—15. http://dx.doi.org/10.1016/j.surfcoat.2015.09.003

13. Larikov L.I., Fel'chenko B.M., Mazarenko V.F., Gurevich C.M., Xarchenko G.K., Anomal'noe uskorenie diffuzii pri impul'snom razrushenii metallov (Abnormal acceleration of diffusion at pulse destruction of metals) // Tekhnich. Fizika. — 1975 (221), no. 5, 1073—1075 (in Russian)

14. Braunovich M., Konchits V.V., Myshkin N.K. Electrical Contacts. Fundamentals, Applications and Technology. — New York: CRC Press. — 2007